Carbon Dial Table Weight Comparison

Composite Materials, Carbon fiber Manufacturing,

The carbon dial table (CDT) has many advantages, but the primary advantage over traditional materials is weight. The low weight of the carbon dial table provides the dial indexer assembly machine manufacturer the opportunity to dramatically reduce table index times.

A Carbon Dial Table with no central through hole is defined as a blank carbon dial table.

The weight of a blank carbon table was determined for CFCD001 material at two core thiknesses 1000(A) and 2000(B) and minimum carbon layer R02. The weight includes the polyurethane edge.

 

Carbon Dial Table compared by weight to the following traditional dial table materials: 1″ thick aluminum and 1″ thick steel.

 

Material: Carbon Fiber
Thickness: (1.15″)

 Material: Aluminum
Thickness: 1.00″		 Material: Steel
Thickness: 1.00″
Rotary Table Diameter Weight (lbs) Weight (lbs) Weight (lbs)
18″ 5 24 72
24″ 8 43 128
30″ 12 68 199
36″ 16 97 287
42″ 22 132 391
48″ 28 173 510
54″ 35 219 646
60″ 42 270 797
66″ 51 327 965
72″ 60 389 1148
78″ 70 457 1347
84″ 80 505 1489

 

 

 

Values of thickness and weight for the blank carbon rotary table are nominal.

  Material CFD001-1000(A)-R02
Thickness, inches
1.15

Material CFCD001-2000(A)-R02
Thickness, inches
2,15
Blank Carbon Dial Table Dial Table Diameter
(in)		 Weight
(lbs)		 Weight
(lbs)
BCDT-01800(A) 18 5 7
BCDT-02400(A) 24 8 11
BCDT-03000(A) 30 12 16
BCDT-03600(A) 36 16 23
BCDT-04200(A) 42 22 30
BCDT-04800(A) 48 28 38
BCDT-05400(A) 54 35 47
BCDT-06000(A) 60 42 57
BCDT-06600(A) 66 51 68
BCDT-07200(A) 72 60 79
BCDT-07800(A) 78 70 92
BCDT-08400(A) 84 80 106

 

 